Midday Mahal Composite Tops

Name: Midday Mahal Composite Tops
Brand: Wilsonart
SKU: 102023778

Composite Surfaces

Overnight

Commercial & Residential

$$$

Beige

Sample size: 4.9 in x 3.4 in x 0.4 in

Arrives tomorrow

Construction: Super-fine layers of Kraft paper are bound together with a phenolic resin and pressed into slabs that are cut, routed, sanded and fabricated into countertops
Content: A nonporous composite material, fabricated from layers of Kraft paper and phenolic resin
Finish: Luster
Format: Panel / Sheet

Dimensional Stability: ISO 4586 tested for Dimensional Stability. Result of 0.3% in the machine direction and 0.7% in the cross direction.
Edge End: Typical shapes in woodworking and Solid Surface applications are obtainable with Wilsonart® Thinscape® Composite Tops, including filleted, thumbnail, flat, and reverse-knife edge profiles
Impact Resistance: ISO 4586 tested for Impact Resistance by a Large Diameter Ball. Result of greater than 78in
Overall Thickness: 0.5
Size: 30 in x 120 in, 30 in x 144 in, 60 in x 120 in, and 60 in x 144 in
Total Weight: 3.77 lbs/sqf

Application Filter: Bath|Countertop|Kitchen|Furniture
Installation: Prior to install, ensure cabinets are leveled. Provide supports every 24in and for overhangs. Shims may be used for assistance. Carbide-tipped saw and router blades should be used for cutting. Use the tool at high speed and feed slowly. Install biscuit slots and biscuits for mitered corners if required. To avoid cracking, radius all corners. Edges should be routered smooth. Postforming is not recommended or approved. Refer to Fabrication Manual for additional information
Recommended Adhesive: Mechanical fasteners are not acceptable. Use a two-part acrylic epoxy adhesive for bonding seams. Devcon Plastic Welder Plexus MA300 or Loctite Epoxy Plastic Bonder work well. 100% silicone sealant is recommended for securing slabs to installation substrates and filling gaps between slabs and terminating substrates. In wet environment applications use mildew-resistant product.
Suitable Substrates: Do not install over a solid substrate. Air movement must be allowed to reach the top and bottom of the slab. Warpage may occur due to changes in temperature and humidity. Where a full substrate is required holes can be cut in the substrate to allow for air movement.

Abrasion Wear Resistance: EN438 tested for Scratch Resistance. Result of 3N. ISO 4586 tested for Surface Wear Resistance. Meets or exceeds 400 cycles
Crazing Resistance: EN438 tested for Crazing Resistance. Grade of 5 for the surface. Grade of 4 for the core.
Flammability: ASTM E-84 Class B
Flexural Strength: EN ISO 178/ASTM 790 tested for Flexural Strength. Result of greater than or equal to 180 Mpa in the machine direction and greater than or equal to 130 Mpa in the cross direction.
Light Blocking: Unknown
Maintenance: To clean the surface, use a damp cloth or sponge and a mild soap or detergent. Rinse thoroughly with warm water and wipe dry. Avoid acidic or abrasive cleaners. A diluted bleach solution can be used as a disinfectant. Reference the Care & Maintenance Guide for additional information
Tensile Strength: EN ISO 527/ASTM 638 tested for Tensile Strength. Result of greater than or equal to 140 Mpa in the machine direction and greater than or equal to 100 Mpa in the cross direction.
Water Resistance: EN438 tested for Boiling Water Immersion and Water Vapor Resistance. Grade of 4

Human Health Impact: CDPH Standard Method v1.2-2017, Low Emitting/Low VOC, UL GREENGUARD, UL GREENGUARD GOLD